Medium Temperature Zinc Phosphating Coating Solution

Zhixing BrandMedium Temperature Zinc-Based Phosphating SolutionZX-314Anti-Rust Phosphating Solution

Product Introduction:

This product is an outstanding member of the zinc-based phosphating solution family, specifically designed for rust prevention. It is easy to use, requires no surface conditioner, does not necessitate strict control of total acid and free acid levels during phosphating, and does not require the separate addition of accelerators. Simply heat to the required temperature range to form a film smoothly.

The working conditions for this product are a phosphating temperature of 65–70°C and a phosphating time of 15–20 minutes. The resulting phosphating film is gray-black, with a fine and uniform appearance, and strong corrosion resistance.

This product is particularly suitable for corrosion-resistant and decorative phosphating of railway bearings, locomotive components, etc., and can serve as medium to long-term rust prevention for steel parts. When stored in a dry environment after phosphating alone, it can last for about half a year. When combined with anti-rust oil, it can remain rust-free for several years.

Usage Method:

Tank Solution Preparation (Calculated for 1 Ton)

According to the ratio of phosphating solution to water = 1:(2-4), add about half of the clean water to the tank, then add one-third of the phosphating solution. Top up with water and heat to the specified process temperature range.

Note: The rust prevention time of phosphating is closely related to the concentration ratio: higher concentration ratios result in longer corrosion resistance but greater consumption. Choose the concentration ratio based on actual needs to achieve the ideal state.

Testing Items:

Appearance: Light green transparent

Copper Sulfate Drop Test: >5 minutes

Film Weight: 10-15g/m²

Treatment Consumption: 10-20m²/kg

Process Flow

Workpiece degreasing and derusting → Water rinsing (better results if heated to around 75°C) → Phosphating (T=70–75°C, soak for 15–20 minutes) → Water rinsing → Air drying

Precautions
(1) Workpiece degreasing and derusting must be thorough.
(2) The workpiece surface should be neutral when entering the working solution.
(3) Replenish the phosphating solution based on consumption, calculated at 10 square meters per kilogram.

(4) The original medium-temperature zinc-based phosphating solution is highly corrosive. Wear rubber gloves and avoid splashing into eyes, mouth, skin, or clothing. In case of accidental contact, rinse immediately with clean water. Seek medical attention if severe.

(5) Store sealed in a cool place. Long-term effective.

Packaging Specifications

25 kg/drum

Special Guidance: After degreasing, rinse the workpiece with water heated to around 75°C, then proceed to phosphating. The phosphating solution should also be heated to 75°C. This treatment ensures optimal results and a thicker phosphating film.